Abstract Objectives: To evaluate the mechanical, physicochemical, and antimicrobial properties of four different formulations containing micro- or nanoparticles of sodium trimetaphosphate (mTMP and nTMP, respectively). Methodology: Four experimental groups were used in this investigation: two mTMP groups and two nTMP groups, each containing zirconium oxide (ZrO2), and solution containing either chitosan or titanium oxide (TiO2) nanoparticles (NPs). Setting time, compression resistance, and radiopacity were estimated. The agar diffusion test was used to assess the antimicrobial activity of the formulations against five different microbial strains: Streptococcus mutans, Lactobacillus casei, Actinomyces israelii, Candida albicans, and Enterococcus faecalis. Parametric and nonparametric tests were performed after evaluating homoscedasticity data (p<0.05). Results: From the properties evaluated, nTMP cements required less setting time and showed greater resistance to compression. Cements containing TiO2 showed greater radiopacity for both nTMP and mTMP. All four cement formulations showed antimicrobial activity against S. mutans and L. casei Conclusion: Formulations containing nTMP have shorter setting times and higher compressive strength, and those with TiO2 nanoparticles showed antimicrobial activities. Clinical relevance: The cement containing nTMP, ZrO2, and TiO2 could be an alternative material for protecting the pulp complex.

ABSTRACT Objective: To investigate the tissue response and the biomineralization ability of CER prepared with epoxy resin or water compared to Mineral Trioxide Aggregate (MTA). Material and Methods: Polyethylene tubes containing materials or empty tubes for control were inserted into the subcutaneous tissues of 30 rats. After 7, 15, 30, 60, and 90 days, the rats were killed and the tubes were removed for analysis using hematoxylin-eosin staining, von Kossa staining, and under polarized light. Inflammation was graded through a score system; the thickness of the fibrous capsule was classified as thin or thick; the biomineralization ability was recorded as present or absent. The results were statistically analyzed using the Kruskal-Wallis test (p<0.05). Results: Histologic analysis performed after 7 and 15 days for CER prepared with epoxy resin or water and for MTA showed moderate inflammation and a thick fibrous capsule (p>0.05). After 30, 60, and 90 days, mild inflammation, and a thin fibrous capsule were observed in all groups (p>0.05). Conclusion: All materials had structures positive for von Kossa and birefringent to polarized light. CER epoxy resin showed biocompatibility and biomineralization similar to CER water and MTA.

Abstract Sources of calcium and phosphate have been added to dental restorative materials to improve their anticaries effect. Objective This study evaluated the effect of adding calcium glycerophosphate (CaGP) to resin-modified glass ionomer cement (RMGIC) on the physico-mechanical properties, ion release, and enamel demineralization. Material and Methods: Specimens were fabricated for each experimental group: RMGIC without CaGP (Control), RMGIC with 1, 3 and 9% CaGP. To determine the release of fluoride (F), calcium (Ca) and phosphorus (P), six specimens were immersed in demineralization and remineralization solutions for 15 days. In another experimental trial, the following physico-mechanical properties were evaluated at time intervals of 1 and 7 days after fabrication: compressive strength (n=12), diametral tensile strength (n=12), surface hardness of material (n=6) and the degree of conversion of monomers (n=8). To study enamel demineralization, specimens (n=12) were attached to enamel blocks and submitted to pH-cycling. Subsequently, surface and cross-sectional hardness and the concentration of F, Ca and P in enamel were determined. Results The addition of CaGP to RMGIC led to higher mean release of F, Ca and P when compared with control (p<0.001). Mechanical properties were within the range of those of the ionomer cements after addition of 1% and 3% CaGP. The degree of conversion did not differ between groups at the 1st and the 7th day (p>0.439). The addition of 3% and 9% CaGP reduced mineral loss and increased F, Ca and P in the enamel when compared with control (p<0.05). Conclusion The addition of 3% CaGP in RMGIC increased the release of F, P and Ca, reduced enamel demineralization, and maintained the physico-mechanical properties within the parameters for this material.

Abstract The present study aimed at evaluating the cytotoxic effects of a novel cement called CER on periodontal fibroblast-like cells of mice (MDPL-20), in comparison with different formulations of Mineral Trioxide Aggregate (MTA), by means of the cell viability test (MTT) and cell morphology analysis. Thirty-two round-shaped samples were fabricated with the following cements: white MTA, white and gray CER and experimental white MTA. The samples were immersed in serum-free culture medium for 24 hours or 7 days (n = 16). The extracts (culture medium + components released from the cements) were applied for 24 hours to previously cultured cells (40.000 cells/cm2) in the wells of 24-well plates. Cells seeded in complete culture medium were used as a negative control. Cell viability was assessed using the MTT assay. Two samples of each cement were used for cell morphology analysis by Scanning Electron Microscopy (SEM). The extracts obtained at the 7-day period presented higher cytotoxicity compared with the 24-hour period (p < 0.05). The gray CER obtained at 24 hours presented the highest cytotoxic effect, whereas the experimental white MTA presented the lowest, similar to the control (p > 0.05). However, at the 7-day period, the experimental white MTA presented no significant difference in comparison with the other cements (p > 0.05). At the 7-day period, CER cement presented cytotoxic effects on fibroblast-like cells, similar to different MTA formulations. However, the immersion period in the culture medium influenced the cytotoxicity of the cements, which was greater for CER cement at 24 hours.

This work presents the results of the investigation of structural and thermal properties of Nd3+-doped tellurite glasses with low OH content. The samples were characterized by XRD, FTIR, DTA, UV/VIS/NIR and Archimedes’ method. Tellurite glasses of composition (100 – x)(0.8TeO2 + 0.2WO3) + xNd2O3 (x = 0, 0.05, 0.5, 1, 2, and 4 mol%) were prepared in both ambient and oxygen atmospheres. All samples showed an increase of the values of Tg, Tx, and Tx-Tg with Nd2O3 addition. The reduction of OH content implies a slight decrease of Tg. The density and the molar volume of the glasses increased with Nd2O3. The intensity of the absorption bands associated with Te-O bonds of TeO4 units decreased compared with the bands associated with Te-O bonds of TeO3+1/3 units. This indicates that Nd2O3 favors the transformation of the TeO4 groups in TeO3 groups via TeO3+1, increasing the NBOs and contributing to the formation of strongly hydrogen-bonded OH groups. The samples made in O2 showed a reduction of 48% of “free” OH ions compared with the Amb ones.

O presente estudo avaliou a ação do trimetafosfato de sódio (TMP) e/ou fluoreto sobre a hidroxiapatita. Pó de hidroxiapatita foi suspenso em diferentes soluções: água deionizada, 500 µg F/mL, 1100 µg F/mL, 1%TMP, 3%TMP, 500 µg F/mL adicionado a 1%TMP e 500 µg F/mL associado a 3%TMP. O pH das soluções foi reduzido para 4,0 e depois de 30 min, elevado para 7,0 (três vezes). Depois do processo de ciclagem de pH, as amostras foram analisadas por difração de raios-X e espectroscopia por infravermelho. As concentrações de fluoreto de cálcio, fluoreto, cálcio e fósforo também foram determinadas. A adição de 1% ou 3% TMP na solução contendo 500 µg F/mL produziu uma maior quantidade de fluoreto de cálcio comparado às amostras tratadas com uma solução de 1100 µg F/mL. A respeito da concentração de cálcio, amostras tratadas com soluções de 1100 µg F/mL e 500 µg F/mL adicionado ao TMP foram estatisticamente similares e mostraram maiores valores. Soluções de 1100 µg F/mL e 500 µg F/mL adicionado ao TMP resultaram em uma proporção molar Ca/P mais próxima à da hidroxiapatita. Conclui-se que a associação de TMP e F favoreceu a precipitação de uma hidroxiapatita mais estável.

The present study analyzed the action of sodium trimetaphosphate (TMP) and/or fluoride on hydroxyapatite. Hydroxyapatite powder was suspended in different solutions: deionized water, 500 µg F/mL, 1,100 µg F/mL, 1%TMP, 3%TMP, 500 µg F/mL plus 1%TMP and 500 µg F/mL plus 3%TMP. The pH value of the solutions was reduced to 4.0 and after 30 min, raised to 7.0 (three times). After pH-cycling, the samples were analyzed by X-ray diffraction and infrared spectroscopy. The concentrations of calcium fluoride, fluoride, calcium and phosphorus were also determined. Adding 1% or 3% TMP to the solution containing 500 µg F/mL produced a higher quantity of calcium fluoride compared to samples prepared in a 1,100 µg F/mL solution. Regarding the calcium concentration, samples prepared in solutions of 1,100 µg F/mL and 500 µg F/mL plus TMP were statistically similar and showed higher values. Using solutions of 1,100 µg F/mL and 500 µg F/mL plus TMP resulted in a calcium/phosphorus ratio close to that of hydroxyapatite. It is concluded that the association of TMP and fluoride favored the precipitation of a more stable hydroxyapatite.

With the increase in life expectancy, biomaterials have become an increasingly important focus of research because they are used to replace parts and functions of the human body, thus contributing to improved quality of life. In the development of new biomaterials, the Ti-15Mo alloy is particularly significant. In this study, the Ti-15Mo alloy was produced using an arc-melting furnace and then characterized by density, X-ray diffraction, optical microscopy, hardness and dynamic elasticity modulus measurements, and cytotoxicity tests. The microstructure was obtained with β predominance. Microhardness, elasticity modulus, and cytotoxicity testing results showed that this material has great potential for use as biomaterial, mainly in orthopedic applications.

OBJECTIVE: This study evaluated the glass transition temperature (Tg) and degree of conversion (DC) of a light-cured (Fill Magic) versus a chemically cured (Concise) orthodontic composite. MATERIAL AND METHODS: Anelastic relaxation spectroscopy was used for the first time to determine the Tg of a dental composite, while the DC was evaluated by infrared spectroscopy. The light-cured composite specimens were irradiated with a commercial LED light-curing unit using different exposure times (40, 90 and 120 s). RESULTS: Fill Magic presented lower Tg than Concise (35-84ºC versus 135ºC), but reached a higher DC. CONCLUSIONS: The results of this study suggest that Fill Magic has lower Tg than Concise due to its higher organic phase content, and that when this light-cured composite is used to bond orthodontic brackets, a minimum energy density of 7.8 J/cm² is necessary to reach adequate conversion level and obtain satisfactory adhesion.

Infrared spectroscopy is one of the most widely used techniques for measurement of conversion degree in dental composites. However, to obtain good quality spectra and quantitative analysis from spectral data, appropriate expertise and knowledge of the technique are mandatory. This paper presents important details to use infrared spectroscopy for determination of the conversion degree.